- Other Plastic Products[1]
- HDPE[2]
- Safety Gloves[3]
- Talc[7]
- Chemical Auxiliary Agent[2]
- Plastic Masterbatches[10]
- Halide ( Except Chloride )[4]
- Other Inorganic Salts[3]
- Other Inorganic Chemicals[2]
- Barite[1]
- Sulphate[1]
- Oxide[3]
- Medical Consumables[2]
- Contact Person : Ms. Zhao Echo
- Company Name : Zibo Zhanheng International Trading Co., Ltd.
- Tel : 0086-533-6072098
- Fax : 0086-533-6205660
- Address : Shandong,Zibo,Yulong building, Huaguang Road NO188
- Country/Region : China
- Zip : 255000
Recycled Plastic Raw material, HDPE (high-density polyethylene) Pipe Grade
Recycled Plastic Raw material, HDPE (high-density polyethylene) Pipe Grade
Appearance: Black Granules
Tensile strength: 10-25
Elongation at break %: 200-500
Heat of fusion J/g: 0.5-20
Ash content: 0.2-0.6
Moisturer: 0.2-0
Black HDPE cable granues for wire sheathing compound or wire jacketing compound as cable materials
SPECIFICATION OF HDPE FOR CABLE SHEATH:
| SPECIFICATION OF HDPE FOR CABLE SHEATH | |||
| PROPERTY | UNIT | SPECIFICATION | TEST |
| Melt Flow Index | g/10min | ≤0.5 | ASTM D1238 |
| Density | g/cm3 | 0.945-0.987 | ASTM D1505 |
| tensile strength | Mpa | ≥20.0 | ASTM D638 |
| Elongation at break | % | ≥650 | ASTM D638 |
| Brittle temperature at low temperature | °C | ≤-76 | ASTM D746 |
| ESCR ,FO | H | ≥500 | ASTM D1693 |
| Oxidation induction period at 200°C | Min | ≥30 | ASTM D3895 |
| Content of Carbon black | % | 2.60±0.25 | ASTM D1603 |
| Carbon Black dispersion | -- | ≥6 | GB2951 |
| Absorption coeffcient | -- | ≥400 | |
| Ceka softening point | °C | ≥110 | ASTM D1525 |
| Dielectric strength | Mv/m | ≥25 | ASTM D149 |
| Volume resistivity | Ω.m | ≥1*1014 | ASTM D257 |
| Dielectric Constant | -- | ≤2.75 | ASTM D1505 |
SPECIFICATION OF LDPE FOR CABLE SHEATH:
Physical Properties | Test Method | Nominal Value | Unit | |
Density | ISO 1183 | 0.921 | g/cm3 | |
Melt Mass-Flow Rate (MFR) | ISO 1133 | 1.9 | g/10min | |
Hardness | ||||
Shore Hardness (shore D) | ISO 868 | 45 | ||
Mechanical Properties | ||||
Tensile Modulus | ISO 527-2 | 175 | MPa | |
Tensile Strength | Yield, | ISO 527-2 | 9.0 | MPa |
Break, | 13.0 | MPa | ||
Tensile Strain(Break) | ISO 527-2 | 850 | % | |
Modulus of Elasticity | Internal Method | 250 | MPa | |
Thermal | ||||
Vicat Softening Temperature | ISO 306/A50 | 89.0 | °C | |
Melting Temperature (DSC) | DIN 53765 | 108 | °C | |
Peak Crystallization Temperature (DSC) | DIN 53765 | 97.0 | °C | |
Heat of Fusion | DIN 53765 | 110 | J/g | |
Electrical | ||||
Volume Resistivity | ASTM D257 | 8.5E+15 | ohm •cm | |
Dielectric Strength | ASTM D149 | 30.0 | kV/mm | |
Dielectric Constant (60Hz) | ASTM D150 | 2.20 | % | |
Dissipation Factor (60 Hz) | ASTM D150 | 0.00050 | ||